LNP™ THERMOCOMP™ DFZ22P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hVUipo_LNPTHERMOCOMPDFZ22Pcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DFZ22P is a compound based on Polycarbonate resin containing Glass Fiber, Milled Glass. Added features of this material include: Exceptional Processing. Also known as: LNP* THERMOCOMP* Compound DF-1004 EP MG Product reorder name: DFZ22P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.61 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.40 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4270 | MPa | ASTM D638 |
| -- | 4410 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 67.6 | MPa | ASTM D638 |
| Fracture | 49.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 6.0 | % | ASTM D638 |
| Fracture | 4.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3380 | MPa | ASTM D790 |
| -- | 3900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 124 | MPa | ASTM D790 |
| -- | 132 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 5.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 560 | J/m | ASTM D4812 |
| 23°C 3 | 52 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.00 | J | ASTM D3763 |
| -- | 8.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 132 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 133 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 381 TFE 15 | RTP Company | PC | RTP |
| VESTAKEEP® L4000G | Evonik Industries AG | PEEK | VESTAKEEP® |
| Axiall PVC 18840 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| CONTINUUM鈩?DMDD-6620 HEALTH+鈩?Datasheet | The Dow Chemical Company | HDPE | CONTINUUM™ |
| K-vinyl 60 Deg C Rating Insulation (80-Wet) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |