LNP™ LUBRICOMP™ JFL36 compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hUzho4_LNP-LUBRICOMP-JFL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* JFL36 is a compound based on Polyethersulfone resin containing 30% Glass Fiber, 15% PTFE. Added featurs of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound JFL-4036 Product reorder name: JFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.30 to 0.60 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.10 to 0.30 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.29 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10200 | MPa | ASTM D638 |
| -- | 9540 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 129 | MPa | ASTM D638 |
| Break | 89.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.9 | % | ASTM D638 |
| Break | 1.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9930 | MPa | ASTM D790 |
| -- | 10800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 179 | MPa | ASTM D790 |
| -- | 138 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.46 | ||
| vs. Itself - Static | 0.36 | ||
| Wear Factor - Washer | 60.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C 2 | 9.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 360 | J/m | ASTM D4812 |
| 23°C 3 | 24 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.40 | J | ASTM D3763 |
| -- | 2.47 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 208 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 210 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.3E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 3.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-325 (Comp) | Ravago Manufacturing Americas, LLC | HDPE | Ravago Compounds |
| MIDILENA III PPJ800 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| Sindustris PP HM5303W | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Ebalta BLH Epoxy 200 / W 400 | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| PLUSTEK RA303G3 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |