NEXT REGRIND ABS 6500-300RG
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | NEXT Specialty Resins, Inc. |
| Trademark: | NEXT REGRIND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hUF0kx_NEXT-REGRIND-ABS-6500-300RG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEXT REGRIND ABS 6500-300RG is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America and is processed by injection molding. The main features of NEXT REGRIND ABS 6500-300RG are:
The typical application fields of NEXT REGRIND ABS 6500-300RG are: furniture |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 3.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1930 | MPa | ASTM D638 |
| Tensile Strength | 40.0 | MPa | ASTM D638 |
| Flexural Modulus | 2140 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 73.9 | °C | ASTM D648 |
| Additional Information |
|---|
| Tensile Elongation at Break, ASTM D790: 280000 psi |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styrolution PS 3600/3601 | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| MonoSol® M1000 | MonoSol, LLC | PVOH | MonoSol® |
| Unichem 7002A-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| Argothane® SS-4031-85 | Argotec LLC | TPU, Unspecified | Argothane® |
| KEBAFORM® C 8027 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |