Sindustris PC GN5102RF
| Category: | PC , Polycarbonate |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hU1O1o_Sindustris-PC-GN5102RF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PC GN5102RF is a Polycarbonate (PC) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PC GN5102RF are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 61.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 30 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 3140 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 98.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 94.0 | °C | ASTM D648 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 235 to 255 | °C | |
| Front Temperature | 250 to 255 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 235 to 265 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.981 to 1.96 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell PE GF 4750 | LyondellBasell Industries | HDPE | Purell |
| Thermylene® P7-60FG-0790 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Karina BLACK PVC COMPOUND-E 70900-48/ 1-E-AC(AS 80 NF)K | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® POM CO GF5 TL5 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |
| Sylvin 2920-93 Green 3170 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |