VECTRA® E820iPd
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hTgLpw_VECTRA-E820iPd.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Catalytically modified E820i Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 in natural at 1.5mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electrical 130°C, mechanical 130°C at 1.5mm. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.79 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.2 | % | ISO 294-4 |
| Flow direction | 0.40 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 89.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.6 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 8800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 120 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 3.2 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 28 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 215 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 119 | °C | ISO 75-2/C |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.9E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dissipation Factor (1 MHz) | 0.016 | IEC 60250 | |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 170 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 315 - 325 | °C | |
| Middle Temperature | 320 - 330 | °C | |
| Front Temperature | 325 - 335 | °C | |
| Nozzle Temperature | 335 - 345 | °C | |
| Processing (Melt) Temp | 335 - 345 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 335 to 345°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SatinFlo™ 60 | Vi-Chem Corporation | PVC, Flexible | SatinFlo™ |
| KumhoSunny PC/ASA HSC7079Z | Shanghai KumhoSunny Plastics Co., Ltd. | ASA+PC | KumhoSunny PC/ASA |
| Karina ORANGE COLOR CONCENTRATE 32/42-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POCAN® DP 7318 000000 | LANXESS GmbH | PBT | POCAN® |
| LNP™ LUBRICOMP™ SP003 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ LUBRICOMP™ |