LNP™ LUBRILOY™ RX05498 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hSwQkR_LNPLUBRILOYRX05498compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* RX05498 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: High Impact. Also known as: LNP* LUBRILOY* Compound RW-HI Product reorder name: RX05498 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 2.4 - 2.6 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.4 - 2.6 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 2.4 - 2.6 | % | ISO 294-4 |
| Flow direction : 24 hours | 2.4 - 2.6 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.70 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2220 | MPa | ASTM D638 |
| -- | 2160 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 60.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2 |
| Fracture | 53.1 | MPa | ASTM D638 |
| Fracture | 54.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 8.0 | % | ASTM D638 |
| Yield | 16 | % | ISO 527-2 |
| Fracture | 31 | % | ASTM D638 |
| Fracture | 64 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2080 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 80.7 | MPa | ASTM D790 |
| -- | 74.6 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.31 | ASTM D3702 Modified | |
| With Self-Static | 0.18 | ASTM D3702 Modified | |
| Wear Factor - Washer | 8.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D256 |
| 23°C 2 | 19 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 140 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 76.0 | J | ASTM D3763 |
| -- | 65.6 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 207 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 189 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 63.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 67.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V51-90 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| HIDEN® P601 KUBLR | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| Laser+® C (E61A) | DAK Americas LLC | PET | Laser+® |
| Latiohm 90/13-09 PD01 G/10 | LATI S.p.A. | PPE+PS | Latiohm |
| Sylvin 8739-65FU White 1395 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |