RONFALIN® ABS 1336 CA
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | A. Schulman Europe |
| Trademark: | RONFALIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hSZ3RO_RONFALINABS1336CA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| General purpose ABS Compound, good flow, constant antistatic. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 32.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 89.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 42.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 28.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.4 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 16 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 2200 | MPa | ISO 178 |
| Flexural Stress 2(4.7% strain) | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 17 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 90.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 78.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ISO 306/A50 |
| -- | 97.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.6 mm | HB | IEC 60695-11-10, -20 | |
| 3.2 mm | HB | IEC 60695-11-10, -20 | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.5 mm | 700 | °C | IEC 60695-2-13 |
| 3.0 mm | 700 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 40 - 80 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TO 323 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Weifang Kingdom CPET101 | Weifang Kingdom Plastic Co., Ltd | CPE | Weifang Kingdom |
| NEFTEKHIM PP 4210G (EP2S30B) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Fainplast EVA 801S | Fainplast Compounds S.r.l | EVA | Fainplast |
| Moplen HP400K | LyondellBasell Industries | PP Homopolymer | Moplen |