LNP™ LUBRICOMP™ LCL36E compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hSQg0c_LNPLUBRICOMPLCL36Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* LCL36E is a compound based on PEEK containing 30% Carbon Fiber and 15% PTFE. Added features of this grade include: Easy Molding, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound LCL-4036 EM Product reorder name: LCL36E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.51 | g/cm³ | ASTM D792 |
| -- | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.31 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.81 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.040 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 21400 | MPa | ASTM D638 |
| -- | 17500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 208 | MPa | ASTM D638 |
| Fracture | 140 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 1.6 | % | ASTM D638 |
| Fracture | 1.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 23000 | MPa | ASTM D790 |
| -- 5 | 22700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 321 | MPa | ISO 178 |
| Fracture, 50.0mm span 6 | 357 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.38 | ASTM D3702 Modified | |
| With Self-Static | 0.38 | ASTM D3702 Modified | |
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 1.55 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Washer | 18.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 83 | J/m | ASTM D256 |
| 23°C 7 | 8.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 650 | J/m | ASTM D4812 |
| 23°C 8 | 42 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 11.0 | J | ASTM D3763 |
| -- | 3.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 342 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 9 | 342 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 332 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 10 | 329 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 1.4E-5 1.4E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 2.9E-5 2.9E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 370 - 380 | °C | |
| Middle Temperature | 380 - 400 | °C | |
| Front Temperature | 380 - 400 | °C | |
| Mold Temperature | 175 - 190 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1005 FR A UV | RTP Company | PBT | RTP |
| HiFill® PA6 GB36 IM1 BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Plaslube® PC / ASA FR1508 UV | Techmer Engineered Solutions | ASA+PC | Plaslube® |
| Polimid B 30 GF V0HFR KW | Poliblend S.p.a. | Nylon 6 | Polimid B |
| VALOX™ DR48 resin | SABIC Innovative Plastics | PBT | VALOX™ |