TOLEN H452 IM
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SIBUR, LLC |
| Trademark: | TOLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hSCSN6_TOLEN-H452-IM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP H452 IM is a polypropylene homopolymer with narrow molecular mass distribution. The product features high fluidity and a special stabilizing package that ensures high processing speed and improved physical and mechanical properties of final products. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 45 | g/10 min | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Yield) | 30.0 | MPa | Internal Method |
| Tensile Strain 2(Yield) | 11 | % | Internal Method |
| Flexural Modulus 3 | 1500 | MPa | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 2.0 | kJ/m² | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | Internal Method |
| Vicat Softening Temperature | 156 | °C | Internal Method 4 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | A (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT REGRIND PA66 3189HSL-300RG | NEXT Specialty Resins, Inc. | Nylon 66 | NEXT REGRIND |
| Caltex PP H430 | GS Caltex | PP Homopolymer | Caltex PP |
| SECCO K4912 | Shanghai SECCO Petrochemical Co., Ltd | PP Random Copolymer | SECCO |
| Hostacom PPU X9067HS C11306 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 8600-75C Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |