Plexiglas® Resist zk5HC

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	Plexiglas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	hQDWSg_Plexiglas-Resist-zk5HC.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Product Profile:
PLEXIGLAS® Resist zk5HC is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).

Typical properties of impact-modified
PLEXIGLAS® molding compounds are

high weather resistance

excellent transmission and clarity

brilliant appearance

the pleasant feel and sound of the moldings.

PLEXIGLAS® Resist zk5HC is characterized by the
following special properties:

high break resistance and impact strength

best resistance to stress cracking of all impact-modified PLEXIGLAS® molding compounds.

Application:
Used for extruding and coextruding sheets and
profiles.

Examples:
extruded/coextruded sheets and profiles for automotive bodies and the sanitaryware sector (bathtubs and shower trays) or crystal-clear
luminaire covers for industrial plants that come into contact with aggressive media.

General Information
Additive	Impact Modifier
Features	Good Weather Resistance High Clarity High ESCR (Stress Crack Resist.) High Impact Resistance Pleasing Surface Appearance
Uses	Automotive Applications Automotive Bumper Automotive Exterior Parts Automotive Exterior Trim Household Goods Housings Profiles Protective Coverings Sheet
Forms	Pellets
Processing Method	Coextrusion Extrusion
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.17	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	0.700	cm³/10min	ISO 1133
Water Absorption			ISO 62
23°C, 24 hr	1.9	%
Equilibrium, 23°C, 50% RH	0.50	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2500	MPa	ISO 527-2/1
Tensile Stress (Yield)	63.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	5.0	%	ISO 527-2/50
Nominal Tensile Strain at Break	28	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	55	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	108	°C	ISO 11357-2
Vicat Softening Temperature	100	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	9.0E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94
Fire Rating	B2		DIN 4102

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ISO 489
Transmittance ¹	92.0	%	ISO 13468-2

Injection	Nominal Value	Unit
Drying Temperature	< 90.0	°C
Drying Time	2.0 to 3.0	hr
Processing (Melt) Temp	220 to 260	°C
Mold Temperature	50.0 to 70.0	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
SNOLEN® EB 0.41/53	JSC Gazprom neftekhim Salavat	HDPE	SNOLEN®
COPYLENE® CH020-01	Phillips 66	PP Homopolymer	COPYLENE®
Gallonprene® GP550-7504	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
ESTABLEND 6500 F	Cossa Polimeri S.r.l.	PC+ABS	ESTABLEND
HiFill® PA6/6 GF14 IM HS L BK	Techmer Engineered Solutions	Nylon 66	HiFill®