LNP™ LUBRICOMP™ Cycoloy_C2801 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hQBTUH_LNP-LUBRICOMP-Cycoloy-C2801-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP™ LUBRICOMP™ CYCOLOY_C2801 compound is a 5% PTFE reinforced PC+ABS, wear resistant, flame retardant compound for moving components in business equipment. Medium heat performance |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.40 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | |
| K (wear) Factor 1 | 430 | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 62.1 | MPa | |
| Break | 51.7 | MPa | |
| Tensile Elongation 3(Break) | 110 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 2720 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 95.1 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.21 | ||
| vs. Steel - Static | 0.16 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 82.2 | °C | ASTM D648 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.49 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 210 to 254 | °C | |
| Middle Temperature | 216 to 260 | °C | |
| Front Temperature | 227 to 274 | °C | |
| Nozzle Temperature | 232 to 274 | °C | |
| Processing (Melt) Temp | 232 to 274 | °C | |
| Mold Temperature | 48.9 to 71.1 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | xE-10, PV=2000 psi-fpm vs Steel |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AVALON® 90 AKU | Huntsman Corporation | TPU, Unspecified | AVALON® |
| CYCOLOY™ CX7240U resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| Europrene® SOL T 6434 | Versalis S.p.A. | SBS | Europrene® |
| Sylvin 9067-90 White 1353 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SABIC® LLDPE M200024 | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |