Adell Polyamide AG-16-662
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Adell Plastics, Inc. |
| Trademark: | Adell Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hPUpXL_Adell-Polyamide-AG-16-662.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Adell Polyamide AG-16-662 is a Polyamide 66 (Nylon 66) material filled with 30% glass fiber. It is available in North America. Primary attribute of Adell Polyamide AG-16-662: Flame Retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.70 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 138 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 9650 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 249 | °C | |
| 1.8 MPa, Unannealed | 232 | °C | |
| Melting Temperature | 254 to 266 | °C | |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (0.710 mm) | 65.0 | °C | UL 746 |
| RTI Imp (0.710 mm) | 65.0 | °C | UL 746 |
| RTI Str (0.710 mm) | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance (3.05 mm) | 60.0 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) (3.05 mm) | 213 | V | UL 746 |
| High Amp Arc Ignition (HAI) (0.100 mm) | 90.0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | UL 746 | ||
| 0.710 mm | 150 | mm/min | |
| 3.05 mm | 115 | mm/min | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.710 mm | 90 | sec | |
| 1.47 mm | 120 | sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 GB 25 | RTP Company | Acetal (POM) Copolymer | RTP |
| AKROMID® A3 GK 30 black (2306) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Hostaform® EC141SXF 10/9022 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Dow Corning® QP1-250 | Dow Corning Corporation | Silicone | Dow Corning® |
| LNP™ LUBRILOY™ K2000 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRILOY™ |