LEXAN™ FST9436 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hP97zA_LEXAN-FST9436-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity opaque, low smoke, and OSU 65/65 compliant PC Copolymer |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 300°C/1.2 kg | 9.00 | cm³/10min | |
| 300°C/5.0 kg | 44.0 | cm³/10min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2260 | MPa | ASTM D638 |
| -- | 2270 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 65.0 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Break 3 | 57.0 | MPa | ASTM D638 |
| Break | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.5 | % | ASTM D638 |
| Yield | 6.3 | % | ISO 527-2/50 |
| Break 5 | 100 | % | ASTM D638 |
| Break | 92 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2340 | MPa | ASTM D790 |
| -- 7 | 2280 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 96.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 102 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 27 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 120 | J/m | ASTM D256 |
| 23°C | 410 | J/m | ASTM D256 |
| -30°C 10 | 13 | kJ/m² | ISO 180/1A |
| 23°C 11 | 22 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 74.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 134 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 131 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ASTM D1525, ISO 306/B120 10 13 |
| -- | 152 | °C | ISO 306/B50 |
| Ball Pressure Test 14(125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.3E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| NBS Smoke Density - Flaming, Dmax | < 40.0 | ASTM E662 | |
| OSU Peak Heat Release Rate 15 | < 65.0 | kW/m² | FAR 25.853 |
| OSU Total Heat Release 16 | < 65.0 | kW·min/m² | FAR 25.853 |
| Vertical Burn Test | FAR 25.853 | ||
| Test a (60 s), passes at | < 15.0 | sec | |
| Test b (12 s), passes at | < 15.0 | sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 260 to 282 | °C | |
| Middle Temperature | 271 to 293 | °C | |
| Front Temperature | 282 to 304 | °C | |
| Nozzle Temperature | 277 to 299 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 71.1 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| 14 . | Approximate maximum |
| 15 . | 5 minute test |
| 16 . | 2 minute test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SWANCOR Epoxy 908 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Badaflex® TPE-S 40A 1000LD | Bada AG | TPE | Badaflex® |
| AVP™ GLT25CP | SABIC Innovative Plastics | PC+PET | AVP™ |
| OnForce™ LFT LF5200-5017 Grey | PolyOne Corporation | Polyolefin, Unspecified | OnForce™ LFT |
| Sylvin 5175-92 Brown 7387 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |