CYCOLOY™ C7410 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hP72df_CYCOLOY-C7410-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLOY C7410 resin is a talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 12.6 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.26 | % | |
| Equilibrium, 23°C, 50% RH | 0.060 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3310 | MPa | ASTM D638 |
| -- | 3350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 54.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/5 |
| Break 3 | 44.0 | MPa | ASTM D638 |
| Break | 38.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.5 | % | ASTM D638 |
| Yield | 3.6 | % | ISO 527-2/5 |
| Break 5 | 74 | % | ASTM D638 |
| Break | 78 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3180 | MPa | ASTM D790 |
| -- 7 | 3270 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 95.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 71 | J/m | ASTM D256 |
| 23°C | 320 | J/m | ASTM D256 |
| -30°C 10 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 31 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 80.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 87.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 83.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ASTM D1525, ISO 306/B50 11 13 |
| -- | 106 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 0.00 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 221 to 254 | °C | |
| Middle Temperature | 221 to 266 | °C | |
| Front Temperature | 243 to 277 | °C | |
| Nozzle Temperature | 243 to 277 | °C | |
| Processing (Melt) Temp | 243 to 277 | °C | |
| Mold Temperature | 60.0 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Verolloy B1500 | PlastxWorld Inc. | ABS+PBT | Verolloy |
| Boda BDF275P | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Elastron® G G500.A80.B.ABS | Elastron USA, Inc. | SEBS | Elastron® G |
| INEOS PP 400-CA70 | INEOS Olefins & Polymers Europe | PP Impact Copolymer | INEOS PP |
| ORIENTENE FM 03 | Oriental Petrochemical Company | PP Homopolymer | ORIENTENE |