Generic COC
| Category: | COC , Cyclic Olefin Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hP41rM_Generic-COC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic COC This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.01 - 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 11 - 44 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 1.50 - 48.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.20 - 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2600 - 3200 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 46.0 - 63.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 1.7 - 4.5 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 50.0 - 2400 | MPa | ISO 527-3 |
| Tensile Stress (Break, 23°C) | 49.1 - 55.3 | MPa | ISO 527-3 |
| Tensile Elongation (Break, 23°C) | 2.2 - 22 | % | ISO 527-3 |
| Elmendorf Tear Strength | 0.088 - 2.4 | N | ISO 6383-2 |
| Water Vapor Transmission Rate (23°C) | 0.025 - 0.10 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.6 - 3.3 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 13 - 20 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 75.0 - 170 | °C | ISO 75-2/B |
| Glass Transition Temperature | 62.0 - 138 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 78.3 - 178 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+14 - 1.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity (23°C) | 2.35 | IEC 60250 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.530 | ISO 489 | |
| Transmittance | 90.0 - 91.0 | % | ASTM D1003 |
| Haze | 0.90 - 3.1 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 50.0 - 102 | °C | |
| Rear Temperature | 205 - 246 | °C | |
| Middle Temperature | 220 - 261 | °C | |
| Front Temperature | 235 - 276 | °C | |
| Nozzle Temperature | 235 - 271 | °C | |
| Processing (Melt) Temp | 220 - 271 | °C | |
| Mold Temperature | 55.0 - 110 | °C | |
| Injection Pressure | 80.0 - 80.2 | MPa | |
| Holding Pressure | 45.0 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic COCThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PP P840 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| ALFATER XL® A65I 2LE0050 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Durethan® BKV 115 H2.0 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Globalene® SE0301 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| Haysite Plastics HTF | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |