AKROMID® B3 GF 25 1 L black (4637)
| Category: | Nylon 6+PP , Polyamide 6 + PP |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hOCTgR_AKROMID-B3-GF-25-1-L-black-4637-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 25 1 L black (4637) is a 25% glass fibre reinforced and heat stabilised polyamide-blend with a reduced density compared to standard PA6 GF 25 Applications are mainly technical components in the automotive and electronic industry, where a weight and cost reduction is required |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.22 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 10.0 | -- | cm³/10min | ISO 1133 |
| Spiral Flow | 86.0 | -- | cm | Internal method |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.80 | -- | % | ISO 294-4 |
| Flow direction | 0.30 | -- | % | ISO 294-4 |
| Humidity Absorption - 62% RH (70°C) | 1.5 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 25 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7500 | 5600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 135 | 88.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.3 | 4.5 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 13 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 15 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 67 | 54 | kJ/m² | ISO 179/1eU |
| 23°C | 68 | 58 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 217 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 198 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 775 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 10 K/min, DSC |
| 2 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIREX® Compound HF3000HG10 | Samyang Corporation | PC | TRIREX® Compound |
| DOMAMID® A1-509-I1-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| ELASTOSIL® LR 3001/55 FR A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Hostacom CR 1171 G1A | LyondellBasell Industries | PP Impact Copolymer | Hostacom |
| LNP™ LUBRICOMP™ DFL24 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |