CYCOLOY™ CM6140 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hO8gO9_CYCOLOYCM6140resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLOY resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffness, balanced properties in flow, impact and heat designed for various thin wall applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.26 | g/cm³ | ASTM D792 |
| -- | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.30 - 0.50 | % | Internal method |
| Transverse flow : 3.20mm | 0.40 - 0.60 | % | Internal method |
| Water Absorption | |||
| 24 hr | 0.10 | % | ASTM D570 |
| 24 hr, 50% RH | 0.010 | % | ASTM D570 |
| Saturated, 23°C | 0.090 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3500 | MPa | ASTM D638 |
| -- | 3200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 65.0 | MPa | ASTM D638 |
| Yield 3 | 65.0 | MPa | ASTM D638 |
| Fracture 4 | 50.0 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 4.0 | % | ASTM D638 |
| Yield | 3.5 | % | ISO 527-2/5 |
| Fracture 6 | 100 | % | ASTM D638 |
| Fracture | 15 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 7 | 3300 | MPa | ASTM D790 |
| -- 8 | 3450 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 97.0 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10 | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 88 | J/m | ASTM D256 |
| 23°C | 200 | J/m | ASTM D256 |
| -30°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 50.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 97.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 83.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 89.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 13 | 80.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 91.0 | °C | ASTM D1525 14 |
| -- | 98.0 | °C | ISO 306/B50 |
| -- | 102 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 5.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.5E+15 | ohms | ASTM D257 |
| Volume Resistivity | 2.7E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.600 mm | V-1 | UL 94 | |
| 0.800 mm | V-0 | UL 94 | |
| 1.50 mm | 5VB | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 850 | °C | IEC 60695-2-13 |
| 3.00 mm | 800 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | > 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 275 - 300 | °C | |
| Middle Temperature | 275 - 300 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 280 - 300 | °C | |
| Processing (Melt) Temp | 275 - 300 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*4 mm |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive XP44-11-1 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| RheTech Polypropylene CC30P255-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| VENELENE® 11Q4 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| Geon™ FIT E 50 | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ FIT |
| OTECH PVC OW135 - Cord Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |