Order Products : sales@su-jiao.com
NORYL™ PX9406P resin
| Category: | PPE , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hMzxvM_NORYLPX9406Presin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL PX9406P resin is an FR (non-halogenated) grade potentially suitable for a variety of electronics applications. RTI (impact) = 105 C. F1 listed in BK color. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2800 | MPa | ASTM D638 |
| -- | 2730 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 76.0 | MPa | ASTM D638 |
| Yield | 76.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 55.0 | MPa | ASTM D638 |
| Fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.7 | % | ASTM D638 |
| Yield | 4.7 | % | ISO 527-2/50 |
| Fracture 5 | 9.7 | % | ASTM D638 |
| Fracture | 9.4 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2840 | MPa | ASTM D790 |
| 6.40 mm | 2840 | MPa | ASTM D790 |
| -- 7 | 2580 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 114 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 113 | MPa | ASTM D790 |
| Yield, 6.40mm | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 60 | J/m | ASTM D256 |
| 23°C | 130 | J/m | ASTM D256 |
| -30°C 10 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 52.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 64.0mm span 12 | 133 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 118 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 122 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 13 | 118 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A120 |
| -- | 140 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 250 | V | IEC 60112 |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm, Testing by SABIC | V-0 | UL 94 | |
| 2.00 mm, Testing by SABIC | 5VB | UL 94 | |
| 2.50 mm, Testing by SABIC | 5VA | UL 94 | |
| Glow Wire Flammability Index (0.750 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 750 | °C | IEC 60695-2-13 |
| 1.50 mm | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 243 - 293 | °C | |
| Middle Temperature | 254 - 299 | °C | |
| Front Temperature | 266 - 304 | °C | |
| Nozzle Temperature | 277 - 304 | °C | |
| Processing (Melt) Temp | 277 - 304 | °C | |
| Mold Temperature | 71.1 - 98.9 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP CESTILITE ASTL | Quadrant Engineering Plastic Products | UHMWPE | Quadrant EPP |
| Royalene® 559 | Lion Copolymer, LLC | EPDM | Royalene® |
| Chemiton GA H2NA 85 | Franplast S.r.l. | SEBS | Chemiton |
| CP PRYME® PC/ABS PCA100 | Chase Plastics Services Inc. | PC+ABS | CP PRYME® PC/ABS |
| Keltan® 9565Q DE | LANXESS Buna GmbH | EPDM | Keltan® |