China PPS hxGR42
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sichuan Deyang Chemical Co., Ltd |
| Trademark: | China PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hMv7FQ_China-PPS-hxGR42.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPS-hxGR42 is toughing & reinforced PPS compound which is filled with glass fiber on the basis of PPS-hx. It shows excellent mechanical properties, high impact strength, high-temperature resistance, solvent resistance, good electrical insulation properties, arc resistance, low water absorption, low mold shrinkage, good dimensional stability and radiation resistance. Its colour is offwhite. Owing to its high performance, it can be used to make appliances where impact resistance is required in automobile, mechanical, electrical and chemical industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) | 9.0 | g/10 min | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 140 | MPa | Internal method |
| Flexural Modulus | 9600 | MPa | Internal method |
| Flexural Strength | 195 | MPa | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 24 | kJ/m² | Internal method |
| Unnotched Izod Impact Strength | No Break | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 285 | °C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | Internal method |
| Volume Resistivity | 2.5E+15 | ohms·cm | Internal method |
| Dielectric Strength | 15 | kV/mm | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Processing (Melt) Temp | 160 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| Injection instructions |
|---|
| Processing time: 2 to 8hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V221-70LG | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Zhongfa PET G30S | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PET | Zhongfa |
| Zytel® 80G33HS1L BK104 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Aplax P2515CN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| DURACON® CH-20 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |