U-polymer UG-100-30
| Category: | Polyarylate , Polyarylate |
| Manufacturer: | UNITIKA Plastics Division |
| Trademark: | U-polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hLXe0T_U-polymer-UG-100-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| U-100 Composite Grade |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.00 mm | 0.10 to 0.20 | % | |
| Across Flow : 3.00 mm | 0.30 to 0.50 | % | |
| Water Absorption (24 hr, 3.18 mm) | 0.24 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 132 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 5700 | MPa | ASTM D790 |
| Flexural Strength | 133 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 180 | °C | ASTM D648 |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.6E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 35 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.015 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 15A4201 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| RTP 6003-75A UV | RTP Company | TPE | RTP |
| NORYL™ EM7430 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| EVERLON® TSO-65 | Ever Polymer Co., Ltd. | SEBS+EPDM | EVERLON® |
| Leona™ 1402G | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |