LNP™ THERMOCOMP™ MF004S compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hLTaro_LNP-THERMOCOMP-MF004S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* MF004S is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound MFX-1004 HS Product reorder name: MF004S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 | % | |
| Across Flow : 24 hr | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 66.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.1 | % | ASTM D638 |
| Flexural Modulus | 4140 | MPa | ASTM D790 |
| Flexural Strength | 107 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 145 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® OM-10160 | Teknor Apex Company | TPE | Monprene® |
| VINIKA® T120D | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| ACCUTECH™ CP0436T40L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Hax™ HF 211 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| CP PRYME® Polystyrene PS100HI-3M | Chase Plastics Services Inc. | PS (HIPS) | CP PRYME® Polystyrene |