SuperLite XLT® SLXLTA.0641BZ
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Azdel, Inc. |
| Trademark: | SuperLite XLT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hKpTfS_SuperLite-XLT-SLXLTA-0641BZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AZDEL SuperLite SLXLTA.0651BZ is a thermoformable, thermoplastic composite sheet comprised of a low- density polypropylene and chopped glass-fiber core, combined with a PET scrim with barrier film attached to one surface and a perforated adhesive film to the other surface. This material is typically used as a substrate in seml- structural applications where a very high strength-to-weight ratio is required, such as in automotive headliners, door panels, rear parcel shelves, sunshades and other interior trim. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | Internal method | ||
| MD : 4.00 mm | 3.3 | kN/m | Internal method |
| MD : 5.00 mm | 4.6 | kN/m | Internal method |
| MD : 6.50 mm | 4.8 | kN/m | Internal method |
| TD : 4.00 mm | 2.3 | kN/m | Internal method |
| TD : 5.00 mm | 2.6 | kN/m | Internal method |
| TD : 6.50 mm | 3.2 | kN/m | Internal method |
| Flexural Strength | Internal method | ||
| MD Peak Load : 4.00 mm | 11 | N | Internal method |
| MD Peak Load : 5.00 mm | 13 | N | Internal method |
| MD Peak Load : 6.50 mm | 12 | N | Internal method |
| TD Peak Load : 4.00 mm | 8 | N | Internal method |
| TD Peak Load : 5.00 mm | 9 | N | Internal method |
| TD Peak Load : 6.50 mm | 9 | N | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| flammability- Self-extinguishing | No |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Base Weight | ASTM D3776 | ||
| Low Density Core | 640 | g/m² | ASTM D3776 |
| Total (including film and scrim) | 750 | g/m² | ASTM D3776 |
| Permeability - Air | None |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Continuous Use Temperature 1 | 90.0 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 35 | mm/min | FMVSS 302 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Free-Loft ratio (maximum, when heated to 205°C): 5.5:1Acoustics (with Fabric) SAE J1400:Sound Absorption Coef. @ 500 Hz = .08Sound Absorption Coef. @ 1000 Hz = .19Sound Absorption Coef. @ 2000 Hz = .44Sound Absorption Coef. @ 4000 Hz = .93 |
| Note Message | |
|---|---|
| 1 . | Maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SWANCOR Epoxy 908 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Ferro PP TPP20AJ25UL BLACK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Geon™ Vinyl Flexible P510 Natural | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| ICORENE® 1505 | ICO Polymers EMEA, A Division of A. Schulman | XLPE | ICORENE® |
| LEXAN™ LUX7632C resin | SABIC Innovative Plastics | PC | LEXAN™ |