ALCOM® PMMA 790/2.1 UV GY1074-11LD3
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® PMMA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hKmNcX_ALCOMPMMA79021UVGY107411LD3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM®PMMA 790/2.1 UV GY1074-11LD3 is a polymethyl methacrylate-acrylic acid product, which contains filler. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. ALCOM®The application fields of PMMA 790/2.1 UV GY1074-11LD3 include automobile industry and lighting equipment. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 5.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2 |
| Tensile Stress | 69.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 3300 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 3.5% strain | 96.0 | MPa | ISO 178 |
| -- | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | 21 | kJ/m² | ISO 179/1eU |
| -40°C | 20 | kJ/m² | ISO 179/1eU |
| -20°C | 20 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 89.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 107 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.0 mm | 650 | °C | IEC 60695-2-12 |
| 2.0 mm | 650 | °C | IEC 60695-2-12 |
| 3.0 mm | 650 | °C | IEC 60695-2-12 |
| 4.0 mm | 650 | °C | IEC 60695-2-12 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 1 | ASTM D1003 | ||
| Total, 1000 µm | 41.4 | % | ASTM D1003 |
| Total, 4000 µm | 4.4 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Dehumidification desiccant | 65 - 90 | °C | |
| Hot air dryer | 65 - 90 | °C | |
| Drying Time | |||
| Dehumidification desiccant | 4.0 - 6.0 | hr | |
| Hot air dryer | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 210 - 280 | °C | |
| Mold Temperature | 50 - 80 | °C |
| Note Message | |
|---|---|
| 1 . | T(Y), A, 2° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unilex™ UP 0120 | United Polychem | LDPE | Unilex™ |
| Adiprene® LF 700D | Chemtura | PUR-Ether/TDI | Adiprene® |
| CYCOLAC™ INP362 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Delta HDPE 5012 | Delta Polymers | HDPE | Delta |
| LNP™ THERMOCOMP™ RF0049S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |