NEXUS PC PCGF10
| Category: | PC , Polycarbonate |
| Manufacturer: | Nexus Resin Group, LLC. |
| Trademark: | NEXUS PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hKWidm_NEXUS-PC-PCGF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Molding Grade PC With 10% Glass |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 65.5 | MPa | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 135 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 288 to 316 | °C | |
| Middle Temperature | 302 to 329 | °C | |
| Front Temperature | 316 to 343 | °C | |
| Nozzle Temperature | 316 to 343 | °C | |
| Processing (Melt) Temp | 316 to 343 | °C | |
| Mold Temperature | 10.0 to 93.3 | °C | |
| Back Pressure | 0.276 to 0.689 | MPa | |
| Screw Speed | 25 to 75 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207B HS UV | RTP Company | Nylon 610 | RTP |
| Aaroprene® TFPP 2020 | Aaron Industries Corp. | PP, Unspecified | Aaroprene® |
| Chemical Resources RPP 3500CW | Chemical Resources, Inc. | PP Random Copolymer | Chemical Resources |
| Hanwha Total PP RB93T | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| LNP™ THERMOCOMP™ UX05504 compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |