SABIC® LDPE 2200H0
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hKVgDo_SABIC-LDPE-2200H0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description SABIC® LDPE 2200H0 is a grade with a low melt flow range and contains no additives. This grade has a good draw down ability and very good optical properties. Application SABIC® LDPE 2200H0 is typically used for thin film applications combining high strength and good optical properties. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.33 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 190 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 190 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 27.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | > 200 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (50.0 µm) | 300 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking - Blown Film (50.0 µm) | 30 | g | Internal method |
| Re-blocking - Blown Film (50.0 µm) | 10 | g | Internal method |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 35.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 40.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 57 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 8.0 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film properties have been measured at film of 50 µm with a BUR of 3.The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA612 A5G7301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 612 | Shandong PA612 |
| Moplen HP422H | LyondellBasell Industries | PP Homopolymer | Moplen |
| Karina WHITE PVC COMPOUND 800-10/61-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1301-8685 | Lehmann & Voss & Co. | PPS | LUVOCOM® |
| POLYCOMPO PE FL60 | POLYCOMPO Co.,Ltd. | LDPE | POLYCOMPO PE |