Mytex® AS319LW-01US
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Mytex Polymers |
| Trademark: | Mytex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hKHgu3_Mytex-AS319LW-01US.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AS319LW-01US is a compounded thermoplastic polyolefin (TPO) designed for exterior automotive applications requiring cold temperature impact, processability and paintability. This product is available in natural, generic black or pre-colored for partial paint applications. Key Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 24 | g/10 min | ISO 1133 |
| Molding Shrinkage 2 | ISO 294-4 | ||
| -- | 5.0E-3 to 7.0E-3 | % | |
| 80°C, 1 hr | 6.0E-3 to 8.0E-3 | % | |
| 121°C, 1 hr | 7.0E-3 to 9.0E-3 | % | |
| Ash Content (600°C) | 19.0 | wt% | ISO 3451-1A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 17.0 | MPa | ISO 527-2/1A/50 |
| Flexural Modulus - Chord 3 | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 46 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact 4(23°C, Max Load) | 16.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 102 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| 2 . | 48 hrs after molding |
| 3 . | 2.0 mm/min |
| 4 . | 2.20 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 307 TFE 15 | RTP Company | PC | RTP |
| Miramid® SE50CW | BASF Leuna GmbH | Nylon 66 | Miramid® |
| E-RIALFILL C HB 20 T | RIALTI Srl | PP Copolymer | E-RIALFILL |
| Hyosung Polyketone M730A | Hyosung Corporation | PK-Aliphatic | Hyosung Polyketone |
| MAGNUM™ 3325 MT | Trinseo | ABS | MAGNUM™ |