Reblend® 6520/OP NERO
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Reblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hK2q7b_Reblend-6520-OP-NERO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS alloy, unreinforced grade |
| General Information | |
|---|---|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 24 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.65 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 50.0 | MPa | |
| Break | 45.0 | MPa | |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 2600 | MPa | ASTM D790 |
| Flexural Strength | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 101 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ASTM D1525 1 |
| -- | 120 | °C | ASTM D1525 2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 230 | °C | |
| Middle Temperature | 250 | °C | |
| Front Temperature | 260 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4092 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Geon™ CPVC EC520 | PolyOne Corporation | CPVC | Geon™ CPVC |
| KPOL-PP K-PPR 42.0 | KPOL Chem Co. | PP Random Copolymer | KPOL-PP |
| Petrothene® GA501022 | LyondellBasell Industries | LLDPE | Petrothene® |
| Sylvin 7844-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |