Amilan® CM3001G30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hI9Abg_Amilan-CM3001G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Amilan® CM3001G30 is a Polyamide 66 (Nylon 66) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Typical application: Automotive. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow : 3.00 mm 1 | 0.60 to 0.90 | -- | % | |
| Flow : 3.00 mm 2 | 0.20 to 0.50 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.60 | -- | % | |
| Saturation, 23°C | 5.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | |||
| M-Scale, 23°C | 97 | -- | ||
| R-Scale, 23°C | 121 | -- | ||
| R-Scale, 80°C | 24 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 235 | 215 | MPa | |
| 23°C | 190 | 140 | MPa | |
| 80°C | 120 | 100 | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C | 2.0 | 2.5 | % | |
| Break, 23°C | 2.5 | 3.0 | % | |
| Break, 80°C | 5.0 | 5.5 | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 11600 | 10500 | MPa | |
| 23°C | 9500 | 6800 | MPa | |
| 80°C | 5800 | 4300 | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 325 | 315 | MPa | |
| 23°C | 290 | 215 | MPa | |
| 80°C | 190 | 135 | MPa | |
| Compressive Stress | ISO 604 | |||
| -40°C | 250 | 200 | MPa | |
| 23°C | 180 | 110 | MPa | |
| 80°C | 110 | 70.0 | MPa | |
| Shear Strength (23°C) | 95.0 | 85.0 | MPa | ASTM D732 |
| Taber Abrasion Resistance (1000 Cycles) | 0.400 | -- | mg | ISO 9352 |
| Coefficient of Friction - vs. Metal 3 | 0.150 | -- | Suzuki Method |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 10 | 12 | kJ/m² | |
| 23°C | 13 | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -40°C | 60 | 70 | kJ/m² | |
| 23°C | 65 | 75 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 262 | -- | °C | ISO 75-2/B |
| Melting Temperature | 265 | -- | °C | DSC |
| CLTE - Flow | 2.0E-5 to 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1800 | -- | J/kg/°C | |
| Thermal Conductivity | 0.40 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 to 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 20 | 17 | kV/mm | IEC 60243-1 |
| Dielectric Constant 4 | IEC 60250 | |||
| 23°C, 50 Hz | 4.60 | 6.30 | ||
| 23°C, 1 kHz | 4.40 | 5.50 | ||
| 23°C, 1 MHz | 3.90 | 4.00 | ||
| Dissipation Factor 5 | IEC 60250 | |||
| 23°C, 50 Hz | 0.020 | 0.080 | ||
| 23°C, 1 kHz | 0.020 | 0.080 | ||
| 23°C, 1 MHz | 0.020 | 0.040 | ||
| Arc Resistance 6 | 114 | 120 | sec | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.794 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | Without Lubrication |
| 4 . | 60% RH |
| 5 . | 60% RH |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2910-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polystyrene Impact 625 | TOTAL Refining & Chemicals | PS (MIPS) | TOTAL Polystyrene |
| ExxonMobil™ PP6262 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Devcon DFense Blok™ Quick Patch | Devcon | Epoxy | Devcon |
| OTECH PVC OW740 - Cord Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |