Hostacom 68F4-3 BLK
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hHz2so_Hostacom68F43BLK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom 68F4-3 BLK fractional melt flow, 3,400 MPa flexural modulus, 30% talc-filled, blow molding and extrusion grade polypropylene homopolymer is typically used for applications that require high strength, stiffness, impact resistance and processability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density 1(23°C) | 1.12 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 33.0 | MPa | |
| Tensile Elongation (Yield, 23°C) | 6.0 | % | |
| Flexural Modulus (23°C) | 3400 | MPa |
| Impact | Nominal Value | Unit | |
|---|---|---|---|
| Notched Izod Impact (23°C) | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 125 | °C |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOPAS® 6015S-04 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| China PPS hx | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| Escorene™ Ultra UL 00018 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Hapflex™ 666-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Plenco 07307 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |