MonoSol® AF L711 Blue 50µ
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hHNDgf_MonoSol-AF-L711-Blue-50-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol AF L711 Blue is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol AF's proprietary blown film technology. MonoSol AF L711 Blue is a grade of PVOH cold water-soluble packaging film engineered for flow wrapping and pleat wrapping of tablets. This film has excellent stiffness for ease of processing on flow wrapping and pleat wrapping equipment. Available thickness range is 20 micron (0.8 mil) to 60 micron (2.4 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Moisture Content (23°C) 1 | 7.4 | wt% | |
| Solubility 2 | |||
| Disintegration : 10°C, 50.8 µm | 27.0 | sec | |
| Disintegration : 24°C, 50.8 µm | 10.0 | sec | |
| Dissolution : 10°C, 50.8 µm | 155.0 | sec | |
| Dissolution : 24°C, 50.8 µm | 93.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (50.0 µm) | 15.6 | m²/kg | ASTM D4321 |
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 20 µm to 60 µm | ||
| Secant Modulus | ASTM D882, ISO 527-3 | ||
| 10%, MD : 51 µm | 68.3 | MPa | |
| 100%, MD : 51 µm | 17.9 | MPa | |
| 10%, TD : 51 µm | 73.8 | MPa | |
| 100%, TD : 51 µm | 19.3 | MPa | |
| Tensile Strength | |||
| MD : Break, 51 µm | 33.8 | MPa | ASTM D882 |
| TD : Break, 51 µm | 45.5 | MPa | ASTM D882 |
| MD : 51 µm | 33.8 | MPa | ISO 527-3 |
| TD : 51 µm | 45.5 | MPa | ISO 527-3 |
| Tensile Elongation | ASTM D882, ISO 527-3 | ||
| MD : Break, 51 µm | 290 | % | |
| TD : Break, 51 µm | 280 | % | |
| Dart Drop Impact (51 µm) | 960 | g | ASTM D1709, DIN 53433 |
| Elmendorf Tear Strength | |||
| MD : 51 µm | 1300 | g | ASTM D1922 |
| TD : 51 µm | 1300 | g | ASTM D1922 |
| MD : 51 µm | 0.13 | N | ISO 6383-2 |
| TD : 51 µm | 0.13 | N | ISO 6383-2 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILAMID® B3 W GB30 | Nilit Plastics | Nylon 6 | NILAMID® |
| Latishield 66-10A | LATI S.p.A. | Nylon 66 | Latishield |
| Hostacom X M2 V05 G61309 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Tunhe PBT TH6085 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBT | Tunhe PBT |
| Lucon® PS6050 | LG Chem Ltd. | ABS | Lucon® |