Tisoplen® PPH 40 MNF TALC
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Tisan |
| Trademark: | Tisoplen® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hGzc15_Tisoplen-PPH-40-MNF-TALC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tisoplen® PPH 40 MNF TALC is a Polypropylene Homopolymer (PP Homopolymer) material filled with 40% talc. It is available in Africa & Middle East or Europe for injection molding. Important attributes of Tisoplen® PPH 40 MNF TALC are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.60 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.010 | % | ISO 62 |
| Ash Content | 40 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 78 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 30.0 | MPa | |
| Break | 29.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 25 | % | |
| Break | 24 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 137 | °C | ISO 75-2/Be |
| Vicat Softening Temperature | 130 | °C | ISO 306/B120 |
| Melting Temperature | 165 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (3.00 mm) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 190 to 210 | °C | |
| Nozzle Temperature | 200 | °C | |
| Processing (Melt) Temp | 170 to 190 | °C | |
| Mold Temperature | 45.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Nylon 7034 B | UBE Engineering Plastics, S.A. | Nylon 612 | UBE Nylon |
| Yanshan PE 1140A | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| HAIPLEN H50 C12 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| EnviroPro 5714G40 | West Michigan Compounding | PP Homopolymer | EnviroPro |
| Monprene® RG-17270 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |