RTP 201E
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hGwOyE_RTP-201E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 200 E Series is based on amorphous nylon. Because it is amorphous it has better dimensional stability than the high crystalline nylons yet retains the desirable properties of the nylon family. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 159 | MPa | ASTM D790 |
| Compressive Strength | 89.6 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 270 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 141 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 127 | °C | ASTM D648 |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.40 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 100 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Molding shrinkage, Linear-flow, ASTM D955, 0.25in: 6mil/in |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 271 - 299 | °C | |
| Middle Temperature | 271 - 299 | °C | |
| Front Temperature | 271 - 299 | °C | |
| Mold Temperature | 65.6 - 98.9 | °C | |
| Injection Pressure | 103 - 124 | MPa | |
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 90 | rpm | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2959-60 White 1541 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SureSpec HP-200NA | Genesis Polymers | PP Homopolymer | SureSpec |
| Bayblend® FR3012 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| HiFill® TPU/I CF10 | Techmer Engineered Solutions | TPU-Polyether | HiFill® |
| LNP™ STAT-KON™ SC004 compound | SABIC Innovative Plastics Europe | Nylon 12 | LNP™ STAT-KON™ |