Plexar® PX1164
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Plexar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hGmwOI_Plexar-PX1164.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s). |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.8 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm, Blown Film | 4.20 | MPa | |
| TD : Yield, 51 µm, Blown Film | 7.40 | MPa | |
| MD : Break, 51 µm, Blown Film | 24.3 | MPa | |
| TD : Break, 51 µm, Blown Film | 27.2 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 51 µm, Blown Film | 14 | % | |
| TD : Yield, 51 µm, Blown Film | 28 | % | |
| MD : Break, 51 µm, Blown Film | 710 | % | |
| TD : Break, 51 µm, Blown Film | 460 | % | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm, Blown Film | 94 | g | |
| TD : 51 µm, Blown Film | 420 | g | |
| Water Vapor Transmission Rate (100% RH, 51 µm, Blown Film) | 61 | g/m²/24 hr | ASTM F372 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 58.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | > 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNTIANHUA® ST-20 | YunNan YunTianHua Co., Ltd. | Acetal (POM) Copolymer | YUNTIANHUA® |
| VECTRA® MT1335 | Celanese Corporation | LCP | VECTRA® |
| Hanwha Total PE EP32 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |
| Karina GREEN PVC COMPOUND 960-40/308-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Monprene® RG-18250 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |