VENYL SFRHG300R
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hGlGoB_VENYL-SFRHG300R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SFRHG300R is a halogen flame retardant compounds UL 94 V0 (conform 2002/95/EC, RoHS directive) 30 % glass fibre reinforced polyamide 6 intended for Injection moulding. APPLICATIONS VENYL SFRHG300R has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL SFRHG300R is available in black (VENYL SFRHG300R-8229) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.54 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 to 0.70 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7000 | 5500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 140 | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 7500 | 4500 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | 14 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 29 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 270 to 285 | °C | |
| Middle Temperature | 265 to 280 | °C | |
| Front Temperature | 260 to 285 | °C | |
| Nozzle Temperature | 265 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203D TFE 10 Z | RTP Company | Nylon 612 | RTP |
| Radilon® A RV300K 100 NAT | Radici Plastics | Nylon 66 | Radilon® |
| Bergamid™ A700 G30 U-S0 BK064 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Generic TES | Generic | TES | Generic |
| Karina YELLOW PVC COMPOUND -E 898-02/160-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |