ALCOM® AWL 15/2 WT1471-04LB
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® AWL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hGeUy8_ALCOMAWL152WT147104LB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM®AWL 15/2 WT1471-04LB is an acrylonitrile butadiene styrene (ABS) product, which contains 15% filler. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. ALCOM®AWL 15/2 WT1471-04LB applications include mirrors, automotive industry and lighting equipment. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 25.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 103 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 38.0 | MPa | ISO 527-2 |
| -- | 38.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 2.0 | % | ISO 527-2 |
| Fracture | 9.0 | % | ISO 527-2 |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 3.5% strain | 62.0 | MPa | ISO 178 |
| -- | 62.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 8.0 | kJ/m² | ISO 179/1eA |
| -40°C | 4.0 | kJ/m² | ISO 179/1eA |
| -20°C | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C | 28 | kJ/m² | ISO 179/1eU |
| -20°C | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 81.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.0 mm | 650 | °C | IEC 60695-2-12 |
| 2.0 mm | 650 | °C | IEC 60695-2-12 |
| 3.0 mm | 650 | °C | IEC 60695-2-12 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tristimulus Value | |||
| Y10 of Reflection | 93 | % | DIN 5033 |
| Y10 of Transmission : 500.0 µm | 0.10 | % | ISO 13468 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Dehumidification desiccant | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| Dehumidification desiccant | 3.0 - 6.0 | hr | |
| Hot air dryer | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 50 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® E FLF 3624 | A. Schulman Europe | PET | SCHULADUR® |
| TCA Lite® 850WMD | Continental Structural Plastics | Polyester, TS | TCA Lite® |
| Vydyne® R533H BK0201 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Xuchuan XCS-2130EN | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Forprene® 6NM001A65 | SO.F.TER. SPA | TPV | Forprene® |