LNP™ STAT-KON™ RE0069S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hGYuge_LNP-STAT-KON-RE0069S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON RE0069S is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Heat Stabilized. Also known as: LNP* STAT-KON* Compound RC-1006 FR HS Product reorder name: RE0069S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.50 | g/cm³ | ASTM D792 |
| -- | 1.49 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.40 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.56 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 27000 | MPa | ASTM D638 |
| -- | 25000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 199 | MPa | ASTM D638 |
| Yield | 207 | MPa | ISO 527-2/5 |
| Break 3 | 199 | MPa | ASTM D638 |
| Break | 207 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.7 | % | ASTM D638 |
| Yield | 1.5 | % | ISO 527-2/5 |
| Break 5 | 1.7 | % | ASTM D638 |
| Break | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 18600 | MPa | ASTM D790 |
| -- 7 | 19600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 324 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 269 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 269 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 77 | J/m | ASTM D256 |
| 23°C 10 | 8.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 11 | 35 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.06 | J | ASTM D3763 |
| -- | 2.48 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 255 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 255 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 242 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 242 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.0E-6 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.0E-6 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0 to 4.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBB106LE | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| NILFLEX® SH A40 MC009 | Taro Plast S.p.A. | SEBS | NILFLEX® |
| Chemical Resources LD2918 | Chemical Resources, Inc. | LDPE | Chemical Resources |
| LNP™ LUBRICOMP™ JX91198 compound | SABIC Innovative Plastics | PESU | LNP™ LUBRICOMP™ |
| Sylvin 3240-65 Red 683 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |