DIAMALOY ENGINEERED ALLOYS PC/PBT 1418
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | DIAMALOY ENGINEERED ALLOYS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hGU6GD_DIAMALOY-ENGINEERED-ALLOYS-PC-PBT-1418.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DIAMALOY ENGINEERED ALLOYS PC/PBT 1418 is a Polycarbonate + PBT (PC+PBT) product. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1 | ASTM D1238 | ||
| 230°C/3.8 kg | 6.0 | g/10 min | |
| 265°C/2.16 kg | 12 | g/10 min | |
| Molding Shrinkage - Flow | 0.70 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 53.8 | MPa | ASTM D638 |
| Tensile Elongation 3(Yield) | 4.6 | % | ASTM D638 |
| Flexural Modulus 4 | 2140 | MPa | ASTM D790B |
| Flexural Strength 5(Yield) | 80.7 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 640 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 105 | °C | ASTM D648 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 6 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 104 to 110 | °C | |
| Drying Time - Desiccant Dryer | 4.0 to 6.0 | hr | |
| Dew Point - Desiccant Dryer | < -28.9 | °C | |
| Suggested Max Moisture | < 0.010 | % | |
| Suggested Shot Size | 60 to 80 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 243 to 266 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 260 to 282 | °C | |
| Nozzle Temperature | 260 to 288 | °C | |
| Melt Temperature (Aim) | 260 | °C | |
| Mold Temperature | 54.4 to 82.2 | °C | |
| Injection Pressure | 68.9 to 138 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 0.345 to 0.517 | MPa | |
| Back Pressure | 0.552 to 1.03 | MPa | |
| Screw Speed | 50 to 75 | rpm | |
| Clamp Tonnage | 4.1 to 6.9 | kN/cm² | |
| Cushion | 2.54 to 7.62 | mm |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Method I (3 point load), 1.3 mm/min |
| 5 . | Method I (3 point load), 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIEL® 5350 | Samyang Corporation | TPEE | TRIEL® |
| DENKA POVAL MP-10 | Denka Company Limited | PVOH | DENKA POVAL |
| Elastollan® 688A10N Film | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyester | Elastollan® |
| EPLAMID 6 GFR 5 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| LARIPUR® LPR 9060EM | COIM S.p.A. | TPU-Polyether | LARIPUR® |