| Radiopaque compound based on Polyamide 12 (PA12). Special mineral filler. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.93 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Transverse flow : 2.00mm | 0.75 - 0.95 | % | ISO 294-4 |
| Flow : 2.00mm | 0.75 - 0.95 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 30.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 0.80 | % | ISO 527-2/5 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 160 | °C | ISO 306/B50 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| HVT | Internal method | ||
| at 120kV | 560.0 | µm | Internal method |
| at 80kV | 140.0 | µm | Internal method |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP556 | Supreme Petrochem Ltd. | PS (IRPS) | SUPREME Specialty PS |
| Huafon JF-D-NC8908 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Karina BLACK PVC COMPOUND 758-48/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Kinta FR2600 | Kinta Technology (Hong Kong) Co., Ltd. | PP, Unspecified | Kinta |
| Hostacom XBR 169 G C12306 | LyondellBasell Industries | PP Copolymer | Hostacom |