Braskem PP CP 204
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hGB2zw_Braskem-PP-CP-204.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: CP 204 is a high melt flow rate heterophasic copolymer with general purpose additive package. This product exhibits excellent processing performance, with good stiffness and impact strength balance. Applications: Thin-walled parts; Easy mould filling; Twisted closures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 92 | ASTM D785 | |
| R-Scale | 92 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 28.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 8.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 1% Secant (Injection Molded) | 1200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C, Injection Molded | 30 | J/m | ASTM D256 |
| 23°C, Injection Molded | 70 | J/m | ASTM D256 |
| -20°C, Injection Molded | 2.9 | kJ/m² | ISO 180 |
| 23°C, Injection Molded | 4.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 89.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 89.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 55.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 152 | °C | ISO 306/A, ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 TFE 10 FR | RTP Company | PC | RTP |
| TEDUR® L 9105-1 | ALBIS PLASTIC GmbH | PPS | TEDUR® |
| VALOX™ 815F resin | SABIC Innovative Plastics Asia Pacific | PBT+PET | VALOX™ |
| LOTTMER SE-130AN | Lotte Chemical Corporation | SEBS | LOTTMER |
| 3M™ Dyneon™ Fluoroelastomer FC 2121 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |