Order Products : sales@su-jiao.com
Generic LCP - Glass Fiber, Long
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hG8KTn_Generic-LCP---Glass-Fiber-Long.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic LCP - Glass Fiber, Long This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 - 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 0.020 - 0.66 | % | ASTM D955 |
| Transverse flow : 23°C | 0.38 - 1.7 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 89 - 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 82.0 - 182 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.5 - 5.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 5600 - 14200 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 85.0 - 158 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 200 - 480 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 267 - 355 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow | 2.0E-6 - 2.4E-6 | cm/cm/°C | ASTM D696 |
| Lateral | 7.2E-5 - 8.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 - 1.2E+15 | ohms·cm | ASTM D257 |
| Dielectric Constant (23°C) | 3.09 - 4.70 | ASTM D150 | |
| Dissipation Factor (23°C) | 3.9E-3 - 0.027 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 135 | °C | |
| Drying Time | 3.0 - 14 | hr | |
| Rear Temperature | 299 - 360 | °C | |
| Middle Temperature | 329 - 380 | °C | |
| Front Temperature | 349 - 400 | °C | |
| Nozzle Temperature | 349 - 400 | °C | |
| Processing (Melt) Temp | 348 - 400 | °C | |
| Injection Pressure | 117 - 140 | MPa | |
| Holding Pressure | 29.5 - 50.0 | MPa | |
| Back Pressure | 2.94 - 3.00 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic LCP - Glass Fiber, LongThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® RG-38135 | Teknor Apex Company | TPE | Monprene® |
| Wanthane® WHT-7180 | Wanhua Chemical Group Co., Ltd. | PC+TPU | Wanthane® |
| NEXT PCR PA6 MG 100PCR | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT PCR |
| NITRIFLEX SB-1502 N | NITRIFLEX | NBR | NITRIFLEX |
| Sylvin 802-88 Red 6287 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |