ENFLEX VU-120-65A
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | ENPLAST, a Ravago Group Company |
| Trademark: | ENFLEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hG2yQU_ENFLEX-VU-120-65A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ENFLEX VU-120-65A is a thermoplastic vulcanized rubber (TPV) product,. It can be processed by extrusion or injection molding and is available in North America or Europe. The main characteristics are: good UV resistance. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 65 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% strain | 2.50 | MPa | ISO 37 |
| 300% strain | 3.70 | MPa | ISO 37 |
| Tensile Stress (Break) | 6.70 | MPa | ISO 37 |
| Tensile Elongation (Break) | 500 | % | ISO 37 |
| Compression Set | ASTM D395B | ||
| 23°C, 72 hr | 24 | % | ASTM D395B |
| 70°C, 22 hr | 33 | % | ASTM D395B |
| 100°C, 22 hr | 35 | % | ASTM D395B |
| Additional Information |
|---|
| The value listed as Density, ISO 1183, was tested in accordance with ISO 2781.Tear Strength, ISO 34-2: 28 kN/mOzone Resistance, ISO 1431: No Crack |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 170 - 180 | °C | |
| Front Temperature | 190 - 200 | °C | |
| Nozzle Temperature | 200 - 210 | °C | |
| Processing (Melt) Temp | 210 - 220 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 195 | °C | |
| Cylinder Zone 4 Temp. | 200 | °C | |
| Cylinder Zone 5 Temp. | 205 | °C |
| Extrusion instructions |
|---|
| Machine Capacity, 30 mm cylinder diameter: 15 to 20 kg/hrMachine Capacity, 45 mm cylinder diameter: 60 to 85 kg/hrMachine Capacity, 60 mm cylinder diameter: 100 to 150 kg/hrMachine Capacity, 90 mm cylinder diameter: 225 to 300 kg/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAMAT 5003D1 | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Clearflex® H&T LGH 138 | Versalis S.p.A. | LLDPE | Clearflex® H&T |
| Fluon® PTFE RB1025S | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| DuraSurf™ SW 2001 | Crown Plastics | UHMWPE | DuraSurf™ |
| NORYL™ GFN2 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |