LNP™ LUBRICOMP™ PFL38S compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hFBZD0_LNP-LUBRICOMP-PFL38S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP PFL38S is a compound based on Nylon 6 resin containing 40% Glass Fiber, 15% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant Also known as: LNP* LUBRICOMP* Compound PFL-4038 HS Product reorder name: PFL38S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C, 48 hr) | 0.30 to 0.40 | % | Internal Method |
| Water Absorption (24 hr, 50% RH) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 152 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 10300 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 220 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 900 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 212 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell PE 1840 H | LyondellBasell Industries | LDPE | Purell |
| DESLON™ 66 DSC203IG6 | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |
| Exelene® HDPE 5502M | Montachem International, Inc. | HDPE | Exelene® HDPE |
| Hanwha Total PP TB53H | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, HMS | Hanwha Total PP |
| HI-ZEX™ 5305E | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |