Hytrel® 6359FG NC010
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hEhObg_Hytrel-6359FG-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 63 Shore D High Performance Polyester Elastomer Developed for Food Contact Applications |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 8.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.5 | % | |
| Flow | 1.5 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.60 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 63 | ||
| Shore D, 15 sec | 58 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 260 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 19.0 | MPa | |
| Break | 41.0 | MPa | |
| 5.0% Strain | 12.0 | MPa | |
| 10% Strain | 15.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 27 | % | |
| Break | > 300 | % |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| Across Flow | 150 | kN/m | |
| Flow | 160 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 15 | kJ/m² | |
| -30°C | 25 | kJ/m² | |
| 23°C, Partial Break | 120 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 19 | kJ/m² | |
| 23°C | 81 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 45.0 | °C | ISO 75-2/A |
| Brittleness Temperature | -100 | °C | ISO 974 |
| Vicat Softening Temperature | |||
| -- | 195 | °C | ISO 306/A50 |
| -- | 100 | °C | ISO 306/B50 |
| Melting Temperature 1 | 211 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.04 | g/cm³ | |
| Specific Heat Capacity of Melt | 2160 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.14 | W/m/K |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LHG204S | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| SureSpec HP-080 | Genesis Polymers | PP Homopolymer | SureSpec |
| Toraycon® 1101G-30 | Toray Resin Company | PBT | Toraycon® |
| TOTAL Polyethylene Lumicene® M 4041 UV | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| Karina BLACK PVC COMPOUND 860-48/ 1-AY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |