LNP™ LUBRILOY™ KL201 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hEczU0_LNPLUBRILOYKL201compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* KL201 is a compound based on Acetal resin containing PTFE, Proprietary Lubricant. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRILOY* Compound KL Product reorder name: KL201 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.41 | g/cm³ | ASTM D792 |
| -- | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 2.5 - 3.0 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.5 - 2.7 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 0.97 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2650 | MPa | ASTM D638 |
| -- | 3050 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 51.6 | MPa | ASTM D638 |
| Yield | 53.0 | MPa | ISO 527-2 |
| Tensile Elongation (Yield) | 20 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 2160 | MPa | ASTM D790 |
| -- | 2260 | MPa | ISO 178 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.30 | ASTM D3702 Modified | |
| With Self-Static | 0.090 | ASTM D3702 Modified | |
| Wear Factor - Washer | 12.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 68 | J/m | ASTM D256 |
| 23°C 2 | 5.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1400 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 157 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 91.7 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 93.4 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 8.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.5E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASTAMID™ KB3EG5 | Marplex Australia Pty. Ltd. | Nylon 6 | ASTAMID™ |
| PELPRENE™ S2001 | TOYOBO America, Inc. | TPEE | PELPRENE™ |
| Axiall PVC 3021 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| NORYL™ NH5020 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Moplen EP549T | LyondellBasell Industries | PP Impact Copolymer | Moplen |