Clearflex® H&T FHH 508
| Category: | LMDPE , Linear Medium Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® H&T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hDVeQI_Clearflex-H-T-FHH-508.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex H&T FHH 508 is an octene copolymer linear medium density polyethylene, with antioxidants, suitable for blown film extrusion. Films obtained from Clearflex H&T FHH 508 show good optical properties, high rigidity, high temperature resistance and excellent sealing properties. Main Application For its excellent optical properties and sealing performances, together with a very low gel content, Clearflex H&T FHH 508 is the ideal choice for the production of lamination films. Due to its softening point, Clearflex H&T FHH 508 is especially recommended for flexible packaging that have to withstand heat cycles such as cook-in films. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 430 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 500 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 16.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 18.0 | MPa | |
| MD : Break, 25 µm, Blown Film | 50.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 40.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 600 | % | |
| TD : Break, 25 µm, Blown Film | 900 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 70 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 30.0 | kN/m | |
| TD : 25.0 µm | 130.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 117 | °C | ISO 306/A |
| Melting Temperature | 127 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 13 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SBB3713 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Grilon® TSG-30/4 FA | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| Lucent TPO TPO-10G | Lucent Polymers, Inc. | Polyolefin, Unspecified | Lucent TPO |
| Eleme NGC250I | Eleme Petrochemical Company Ltd | PP Impact Copolymer | Eleme |
| For-Tec E OC7OAN (Series: AD/PAX/CR) | KRAIBURG TPE | TPE | For-Tec E |