RTP 3407-4
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hCak7X_RTP-3407-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. The 3400 Series is based on a self-reinforcing crystalline polymer. Liquid crystal polymers offer outstanding heat and chemical resistance. Its unique properties combined with excellent flowability give these compounds a wide range of applications. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.030 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19300 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 148 | MPa | |
| -- | 103 | MPa | |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 15900 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- | 145 | MPa | |
| Yield | 214 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 270 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 321 | °C | ASTM D648 |
| RTI Elec | UL 746 | ||
| 0.305 mm | 130 | °C | |
| 1.59 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 0.305 mm | 130 | °C | |
| 1.59 mm | 130 | °C | |
| RTI Str | UL 746 | ||
| 0.305 mm | 130 | °C | |
| 1.59 mm | 130 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 26 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.024 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.305 mm, BK, NC | V-0 | ||
| 1.59 mm, BK, NC | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 360 to 391 | °C | |
| Middle Temperature | 360 to 391 | °C | |
| Front Temperature | 360 to 391 | °C | |
| Nozzle Temperature | 343 to 379 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Injection Pressure | 55.2 to 124 | MPa | |
| Clamp Tonnage | 5.5 to 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® C C130 U | A. Schulman Europe | PC+ABS | RONFALIN® C |
| Sylvin 2912-57 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Elastron® V V601.A80.N | Elastron USA, Inc. | TPV | Elastron® V |
| Kingfa API-1925 | Kingfa | PP, Unspecified | Kingfa |
| Moplen HP648H | LyondellBasell Industries | PP Homopolymer | Moplen |