Fiberfil® J-60/10/E8
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hC9GMS_Fiberfil-J-60-10-E8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil® J-60/10/E8 is a Polypropylene Homopolymer (PP Homopolymer) material filled with 10% glass fiber. It is available in North America. Important attributes of Fiberfil® J-60/10/E8 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.60 | % | |
| 6.35 mm | 0.60 | % | |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 to 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3030 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 58.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 4.5 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 2690 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 149 | °C | |
| 1.8 MPa, Unannealed | 138 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LS01018 - BO | Premier Polymers, LLC. | LLDPE | Premier |
| RTP ESD C 1080 TFE 15 | RTP Company | PBT | RTP |
| Versaflex™ CL2242 | PolyOne Corporation | TPE | Versaflex™ |
| Thermylon® N3-33FG-1626 | Asahi Kasei Plastics North America Inc. | Nylon 66 | Thermylon® |
| Celstran® PA66-GF50-02 P11 | Celanese Corporation | Nylon 66 | Celstran® |