PAmpellonne® 601s
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Politem Plastik Ltd. |
| Trademark: | PAmpellonne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hBbEiG_PAmpellonne-601s.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| All Politem Plastik Polyamide Resins are recycled from Post Industrial Fiber Waste Streams |
| General Information | |
|---|---|
| Recycled Content |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 to 1.14 | g/cm³ | ISO 1183 |
| Ash Content | 0.30 to 0.50 | % | ISO 3451-4 |
| Moisture | 0.10 to 0.30 | % | ISO 15512/B |
| Relative Viscosity 1 | 2.60 to 2.80 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| DSC Analysis | > 96 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 85 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 to 4000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 80.0 to 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 5.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 to 7.0 | kJ/m² | ISO 179/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 220 to 225 | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Formic |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4083 TFE 13 SI 2 | RTP Company | PPA | RTP |
| Tenogel® ABS A3 HS NTLA013 AB329 | Petropol Industry and Trade of Polymers LTDA | ABS | Tenogel® ABS |
| APEX® 1013 | Teknor Apex Company | PVC, Semi-Rigid | APEX® |
| HiFill® PA6/6 GF33 IM HS L BK001 | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| PETILEN F2-21T | PETKIM Petrokimya Holding A.S. | LDPE | PETILEN |