SUMIKASUPER® LCP E6008
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Sumitomo Chemical Co., Ltd. |
| Trademark: | SUMIKASUPER® LCP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hBUvFd_SUMIKASUPER-LCP-E6008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKASUPER LCP is a thermotropic liquid crystalline polyester, showing the highest heat resistance among engineering plastics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.18 | % | |
| Across Flow | 1.2 | % | |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 147 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.2 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 23°C | 12300 | MPa | |
| 200°C | 4900 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Yield, 23°C | 143 | MPa | |
| Yield, 200°C | 33.0 | MPa | |
| Shear Strength | 51.0 | MPa | ASTM D732 |
| Poisson's Ratio | 0.46 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.40 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.40 mm) | 410 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 279 | °C | ASTM D648 |
| CLTE | Internal Method | ||
| Flow : 150°C | 1.3E-5 | cm/cm/°C | |
| Transverse : 150°C | 5.6E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.52 | W/m/K | JIS R2618 |
| RTI Elec (3.20 mm) | 220 | °C | UL 746 |
| RTI Imp (3.20 mm) | 200 | °C | UL 746 |
| RTI Str (3.20 mm) | 240 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 4.40 | ||
| 1 MHz | 3.90 | ||
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 0.022 | ||
| 1 MHz | 0.032 | ||
| Arc Resistance | 130 | sec | ASTM D495 |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.300 mm, ALL) | V-0 | UL 94 | |
| Oxygen Index | 48 | % | JIS K7201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Soldering Resistance | 300 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 320 to 350 | °C | |
| Front Temperature | 340 to 370 | °C | |
| Nozzle Temperature | 340 to 370 | °C | |
| Processing (Melt) Temp | 350 | °C | |
| Mold Temperature | 40.0 to 160 | °C | |
| Injection Pressure | 80.0 to 160 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 20.0 to 40.0 | MPa | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoMid B330 | TechnoCompound GmbH | Nylon 6 | TechnoMid |
| NEO-ZEX™ 2024G | Prime Polymer Co., Ltd. | LLDPE | NEO-ZEX™ |
| Chemical Resources LD15920 | Chemical Resources, Inc. | LDPE | Chemical Resources |
| Karina WHITE PVC COMPOUND 900-10/ 1-P-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PETOPLEN EH 241 | PETKIM Petrokimya Holding A.S. | PP, Unspecified | PETOPLEN |