Witcom PA6 3C-HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hB7XRD_Witcom-PA6-3C-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PA6 3C-HS is a Polyamide 6 (Nylon 6) product filled with 15% carbon fiber. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 to 0.40 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 8.0 | % | |
| Equilibrium, 23°C, 50% RH | 2.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 180 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 to 3.0 | % | ISO 527-2 |
| Flexural Modulus | 9500 | MPa | ISO 178 |
| Flexural Stress | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 195 | °C | ISO 75-2/A |
| CLTE - Flow | 2.9E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 95.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 to 1.0E+6 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 750 | °C | IEC 60695-2-12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1183A | Teknor Apex Company | TPE | Telcar® |
| EMOPLEN® A 1308 T2 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| Latene® AG3H2W G/30-V0E | LATI S.p.A. | PP Homopolymer | Latene® |
| ISORENE™ A6-1001 | SABIC Innovative Plastics Europe | TPE | ISORENE™ |
| LNP™ STAT-KON™ DX09301C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |